INSULATION MASTICS
METRO SUPPLY COMPANY IS A STOCKING DISTRIBUTOR OF CHILDERS INSULATION MASTICS AND SEALANTS
|
|
|
CHILDERS CP-9 AK-CRYL MASTIC COATING
|
|
(WATER BASED)
DESCRIPTION:
Childers AK-CRYL CP-9 is a polymeric, water based weather barrier, breather type mastic. CP-9 dries to a tough flexible film that protects thermal insulation from the ravages of weather by preventing water, rain, snow, sleet, spillage, wash water, etc., from entering into the system. In addition, CP-9 provides protection from mechanical damage created by external forces such as impact abrasion as well as the internal forces of thermal expansion, contraction, or vibration. Using CP-9 can also protect the insulation from chemical attack of acids, alkalis and solvents. CP-9 is fire resistant and U.V. stable.
|
USES:
Childers AK-CRYL CP-9 Weather Barrier Coating provides weatherproofing and mechanical protection of thermal insulation both outdoors and indoors, in hot, cold and dual-temperature service. Because it is a ‘breather’ coating (vapors under pressure will pass through it), it should only be used over insulations in low temperature, or dual-temperature service when the insulations themselves are vapor barriers, or where a complete vapor barrier system is applied to the insulated surface either before or after the coating is applied.
COLOR:
White
SERVICE TEMPERATURE RANGE:
-40ºF to 180ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
Touch–2-4 hours
Through–24 to 36 hours
COVERAGE:
6 U.S. gal./100 sf
CLEAN-UP:
Warm, soapy water (wet), xylol (dry)
WATER VAPOR PERMEANCE ASTM E-96
Greater than 1.0 perms (Procedure B) at 1/16” film thickness.
|
|
|
CHILDERS CP-10 VI-CRYL MASTIC COATING
|
|
(Trowel Grade)
DESCRIPTION:
Childers VI-CRYL CP-10 weather barrier coating is a tough, durable, and fire-resistive water based mastic for most types of thermal insulation and finishing and insulating cements. It is very thixotropic - it looks heavy but spreads easily. It is available in a variety of standard and special faderesistant colors. It is outdoor rated and U.V. resistant.
|
USES:
VI-CRYL CP-10 weather barrier coating is unsurpassed for the mechanical protection and weatherproofing of thermal insulations both outdoors and indoors, in hot, cold, and dual-temperature service. However, since it is a ‘breathing’ coating (vapors under pressure will pass through it) it should only be used over insulations in lowtemperature, or dual-temperature service when the insulations themselves are vapor barriers. VI-CRYL CP-10 has also found use throughout the thermal insulation industry as a coating used over closed cell polyethylene and polyurethane foam insulations. Industry experience has demonstrated that all weather barrier coatings may blister when applied over polystyrene board. This effect may be limited by the use of white colored coatings. VI-CRYL CP-10 weather barrier coating in its Metallic Gray color is the ideal companion product to Aluminum and Stainless Steel Jacketing.
COLORS:
White
Metallic Gray
Black
SERVICE TEMPERATURE RANGE:
-40ºF to 180ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
Touch–2-4 hours
Through–24 to 36 hours
COVERAGE:
6 U.S. gal./100 sf
CLEAN-UP:
Warm, soapy water (wet) xylol (dry)
WATER VAPOR PERMEANCE ASTM E-96
Greater than 1.0 perm for 1/16 inch dry film. (Procedure B)
|
|
|
CHILDERS CP-11 VI-CRYL MASTIC COATING
|
|
(Brush Grade)
DESCRIPTION:
Childers' VI-CRYL CP-11 weather barrier coating is a tough, durable, and fire-resistive water based mastic for most types of thermal insulation and finishing and insulating cements. It is very thixotropic - it looks heavy but spreads easily. It is available in a variety of standard and special fade resistant colors. It is outdoor rated and U.V. resistant.
|
USES:
VI-CRYL CP-11 weather barrier coating is unsurpassed for the mechanical protection and weatherproofing of thermal insulations both outdoors and indoors, in hot, cold, and dual-temperature service. However, since it is a ‘breathing’ coating (vapors under pressure will pass through it) it should only be used over insulations in lowtemperature, or dual-temperature service when the insulations themselves are vapor barriers. VI-CRYL CP-11 has also found use throughout the thermal insulation industry as a coating used over closed cell polyethylene and polyurethane foam insulations. Industry experience has demonstrated that all weather barrier coatings may blister when applied over polystyrene board. This effect may be limited by the use of white colored coatings.
*VI-CRYL CP-11 weather barrier coating in its Metallic Gray color is the ideal companion product to Aluminum and Stainless Steel Jacketing.
COLORS:
White
Metallic Gray
Black
SERVICE TEMPERATURE RANGE:
-40ºF to 180ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
Touch–2-4 hours
Through–24 to 36 hours
COVERAGE:
6 U.S. gal./100 sf
CLEAN-UP:
Warm, soapy water (wet) xylol (dry)
WATER VAPOR PERMEANCE ASTM E-96
Greater than 1.0 perm for 1/16 inch dry film. (Procedure B)
|
|
|
CHILDERS CP-22 / CP-24 CHIL-PRUF
|
|
ASPHALT BASED FIBRATED CUTBACK VAPOR BARRIER AND WEATHER BARRIER INSULATION COATING
DESCRIPTION:
Childers CHIL-PRUF CP-22/24 is an effective asphalt based cutback fibrated vapor barrier coating for use over insulations on piping and equipment operating at low to moderately high temperatures. Properly applied, CHIL-PRUF vapor barrier coating provides protection against atmospheric corrosives, chemical dusts, fumes, fogs, and moisture. The cured coating forms a highly impermeable, tough, durable, and well-bonded finish.
|
USES:
Childers CHIL-PRUF CP-22/24 vapor barrier coating has a broad application range as a vapor and weather barrier over many types of insulations, including fibrous glass, polyurethane foams, glass foams, and other low temperature insulation materials. It is not to be used with polystyrene foam insulation. CHIL-PRUF vapor barrier coating is recommended for use in cold and dual temperature service. As a vapor barrier coating, it is used to protect insulation over fittings, piping, tanks and tank heads, process vessels, and equipment. CHIL-PRUF vapor barrier coating also provides protection for insulation applied on underground pipelines.
PRODUCT GRADES:
CP-22 Trowel Grade
CP-24 Heavy Duty Airless Spray Grade
COLOR:
Black
SERVICE TEMPERATURE RANGE:
-60ºF to 325ºF
APPLICATION TEMPERATURE RANGE:
50ºF to 100ºF
DRYING TIME:
Touch–2-4 hours
Through–24 to 36 hours
COVERAGE:
Varies with substrate and membrane.
9.7-12.7 U.S. gal./100 sf
CLEAN-UP:
Mineral spirits (flammable), chlorinated solvent (non-flammable)
WATER VAPOR PERMEANCE ASTM E-96
0.02 to .03 perms (Procedure E)
@ .094” thickness
SURFACE BURNING CHARACTERISTICS:
(ASTM E-84, Tunnel Test)
Surface: Inorganic reinforced cement board
Flame Spread Index: 150
|
|
|
CHILDERS CP-25 CHIL-BRATE
|
|
WATER BASED FIBRATED ASPHALT EMULSION WEATHER BARRIER INSULATION COATING
DESCRIPTION:
Childers CHIL-BRATE CP-25 is a water based fire retardant fibrated asphalt emulsion weather barrier coating for use over insulations on above ground installations operating at moderate to high temperature service. Since it is a “breathing” coating, vapors under pressure will pass through it. When dry, the film is tough and durable. It provides protection against atmospheric corrosives, chemical liquids, and fumes.
|
USES:
Childers CHIL-BRATE CP-25 weather barrier coating is primarily designed to protect insulation on equipment and structures in high temperature service, although it also provides protection against corrosion when applied directly over steel and concrete. Typical insulations protected with CHIL-BRATE weather barrier coating include calcium silicate, mineral and glass fibers, polyurethane, and foamglas.
COLOR:
Black
SERVICE TEMPERATURE RANGE:
-20ºF to 200ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
24-48 hours
COVERAGE:
15 gallons per 100 sf
CLEAN-UP:
Clean water, followed by mineral spirits.
|
|
|
CHILDERS CP-30 CHIL-PERM LO
|
|
LOW ODER VAPOR BARRIER COATING FOR INDOOR APPLICATIONS
DESCRIPTION:
Childers CHIL-PERM CP-30 LO is an extremely effective vapor barrier coating for all low temperature applications. In the wet state, it has an unusual consistency which allows it to be buttered-on in relatively heavy films, or it can be brushed out into thin films. It is made with an elastomeric resin which yields a tough, yet flexible, dry film with excellent adhesive properties.
|
USES:
Childers CHIL-PERM CP-30 LO Vapor Barrier Coating, in the dry state, is a fire resistive, flexible coating for all types of thermal insulations in cold and dual temperature service. As an indoor vapor barrier coating, it is used to vapor seal fittings, piping, and equipment insulated with fibrous glass, polyurethane foams, and other low temperature insulation materials. It is not to be used in direct contact with polystyrene foams. CP-30 LO coating is used as a barrier at the butt joints of pipe and block insulation where intermediate vapor stops are required. CP-30 LO coating is also used to seal the joints of foil-faced boards and other factory vapor sealed insulation material, and also where pins and staples puncture insulation vapor barrier facings.
COLOR:
White
SERVICE TEMPERATURE RANGE:
-40ºF to 190ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
To Touch–8 hours
Through–24 to 36 hours
FLASH POINT:
107ºF
COVERAGE:
4 U.S. Gals./100 sf
CLEAN-UP:
Non-flammable–Chlorinated Solvents Flammable–Xylene
WATER VAPOR PERMEANCE (ASTM E-96):
ASTM E-96 Procedure B, Less than 0.02 perms at 0.02 inch film thickness.
|
|
|
CHILDERS CP-33 CHIL-OUT
INDOOR & OUTDOOR WATER BASED VAPOR RETARDER COATING
|
|
DESCRIPTION:
Childers CP-33 is a water-based vapor retarder coating for insulation on interior and exterior, low temperature and some dual temperature applications such as chilled water and refrigerated pipe lines, HVAC ducts and low temperature equipment. It is fast drying and forms a tough, flexible dry film which protects insulated surfaces and helps retard the flow of vapor through an insulation system. It has a smooth, creamy consistency that spreads easily and can be applied in a relatively heavy coating or brushed out into a thin, smooth film.
|
USES:
Childers CP-33 can be used on most types of thermal insulations in both cold and dual temperature service. It is used to vapor seal the seams, overlaps and punctures from pins and staples in FSK, ASJ, white paper and polyester vapor barrier facings on insulation boards, duct wrap and pipe covering. It may also be used to seal cut ends of insulation to prevent moisture ingress and fiber release. It is compatible with fiber glass, mineral fiber, cellular glass, polyisocyanurate, polyurethane, polystyrene, phenolic, rubber foam and other insulations.
COLOR:
White
SERVICE TEMPERATURE RANGE:
-20ºF to 100ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
To Touch–3 Hours
Through–24 Hours
COVERAGE:
4 U.S. gal. / 100 sf
CLEAN-UP:
Warm, soapy water while coating is still wet.
WATER VAPOR PERMEANCE (ASTM F-1249):
0.15 Perms @ 28 mils Dry film thickness. Tested at 100ºF, 90% RH
0.07 Perms @ 41 mils DFT. Tested at 70ºF, 50% RH.
SURFACE BURNING CHARACTERISTICS ASTM E-84
Flame Spread 5
Smoke Developed 0
|
|
|
CHILDERS CP-34 VAPOR RETARDANT COATING
|
|
DESCRIPTION:
Childers CP-34 is a water based vapor retarder coating for use over many types of thermal insulation including polystyrene foam. It is ideal for use over ASJ, FRK and FSK jackets and board facings to provide a vapor retarding seal at joints, laps and weld pin punctures.
CP-34 is formulated for indoor and outdoor commercial use. It has a mild latex “paint type” odor and is designed for use on pipes, vessels, ducts and equipment operating between 32°F (0°C) and ambient temperatures. CP-34 has a WVTR rating in the range of other competitive water based vapor barrier coatings. For heavier duty commercial or industrial use select Childers CP-35.
|
USES:
Childers CP-33 can be used on most types of thermal insulations in both cold and dual temperature service. It is used to vapor seal the seams, overlaps and punctures from pins and staples in FSK, ASJ, white paper and polyester vapor barrier facings on insulation boards, duct wrap and pipe covering. It may also be used to seal cut ends of insulation to prevent moisture ingress and fiber release. It is compatible with fiber glass, mineral fiber, cellular glass, polyisocyanurate, polyurethane, polystyrene, phenolic, rubber foam and other insulations.
COLOR:
White
SERVICE TEMPERATURE LIMITS:
-20°F to 180°F
DRYING TIME:
To Touch–4 hours
Through–24 hours
COVERAGE:
4 gallons/100 sf
WATER VAPOR PERMEANCE:
ASTM F 1249, 0.08 perms at 45 mils dry. Tested at 100°F and 50% RH.
WET FLAMMABILITY (ASTM D3278)
Flash Point: None to boiling, 212°F
|
|
|
CHILDERS CP-35 CHIL-PERM WB
|
|
INDOOR & OUTDOOR WATER BASED VAPOR RETARDER COATING
DESCRIPTION:
Childers CHIL-PERM WB CP-35 is an effective, high performance, water based, vapor retarder coating designed for all interior and exterior, low temperature and some dual temperature applications. It is fast drying and forms a tough, flexible dry film which retards the flow of vapor through an insulation system. It looks heavy, but spreads easily. It can be applied in a relatively heavy film or brushed out into a thin, smooth film.
|
USES:
Childers CHIL-PERM WB CP-35 is effective on all types of thermal insulations in both cold and dual temperature service. As a vapor retarder coating, it is safely used to vapor seal fittings, piping, and equipment insulated with mineral fiber, cellular glass, polyisocyanurate, polyurethane, polystyrene, phenolic, and even open cell polyethylene foams. It may also be used to seal the joints of foil-faced boards and other factory vapor sealed insulation materials, (test before using for this application) as well as to seal punctures from pins and staples in vapor barrier facing materials.
COLOR:
White
SERVICE TEMPERATURE LIMITS:
-20°F to 190°F
APPLICATION & STORAGE TEMPERATURE RANGE:
50ºF to 100ºF
DRYING TIME:
To Touch–3 hours
Through–24 to 36 hours
COVERAGE:
4 to 6 U.S. gal./100 sf
CLEAN-UP:
Warm, soapy water while coating is still wet.
WATER VAPOR PERMEANCE ASTM F-1249
0.09 Perms (0.06 metric perms) @ 55 mils Dry film thickness. Tested at 73ºF, 50% RH
SURFACE BURNING CHARACTERISTICS ASTM E-84
Flame Spread 0
Smoke Developed 0
|
|
|
CHILDERS CP-38 CHIL-LOW
VAPOR RETARDER
|
|
DESCRIPTION:
Childers CP-38 is a water-based, high solids, flexible, vapor retarder coating for use over many types of thermal insulation including polystyrene foam. It can also be used over dry concrete and insulating cement to provide a vapor retarder coating.
Childers CP-38 is formulated for indoor and outdoor commercial use and light duty industrial use. It is UV resistant and has a mild latex “paint type” odor. CP-38 is designed for use on pipes, vessels, ducts and equipment operating at cryogenic up to ambient temperatures. It is non-flammable in the wet state and fire resistive when dry.
|
Childers CP-38 is ideal for use over ASJ, FRK and FSK jackets and board facings to give a vapor retarding seal at joints, laps and over staples and weld pin punctures. It can also be used as a duct board closure sealant.
COLOR:
White
SERVICE TEMPERATURE LIMITS:
-20°F to 180°F
DRYING TIME:
To Touch–4 hours
Through–24 hours
COVERAGE:
4 gallons/100 sf
WATER VAPOR PERMEANCE:
ASTM E 96 Procedure B, 0.01 perms at 43 mils dry.
ASTM F 1249, 0.08 perms at 37 mils dry. Tested at 100ºF and 90% RH.
WET FLAMMABILITY:
Flash Point: None to boiling, 212°F
SURFACE BURNING CHARACTERISTICS (ASTM E-84)
Flame Spread 15
Smoke Develop 30
|
|
|
CHILDERS CP-40 ENCACEL X
|
|
VAPOR BARRIER AND WEATHERPROOFING COATING FOR INTERIOR AND EXTERIOR APPLICATIONS
DESCRIPTION:
Childers ENCACEL X CP-40 is an elastomeric polymer-based coating designed for the protection of thermal insulation. ENCACEL X CP-40 Vapor Barrier Coating has good vapor barrier properties as well as excellent resistance to chemicals, low temperature flexibility, and superior adhesive characteristics.
|
USES:
Childers ENCACEL X CP-40 Vapor Barrier Coating provides a tough, flexible, fire-resistant finish. It is recommended for hot and cold exterior applications where the chemical environment necessitates additional protection. It is not to be used in direct contact with polystyrene foam insulation. It may be used with most other types of insulation.
COLOR:
CP-40 White, Trowel/Glove
CP-40-1 Gray, Trowel/Glove
SERVICE TEMPERATURE RANGE:
-50ºF to 220ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
Touch–5 hours
Through–48 hours
COVERAGE:
5 gal./100 sf
CLEAN-UP:
Xylene
WATER VAPOR PERMEANCE:
ASTM F 1249, 0.03 perms at 30 mils dry. Tested at 100ºF and 90% RH.
|
|
|
CHILDERS CP-45 ENCACEL V
|
|
VAPOR BARRIER AND WEATHERPROOFING COATING FOR INTERIOR AND EXTERIOR APPLICATIONS
DESCRIPTION:
Childers ENCACEL V, CP-45, is an elastomeric polymer-based vapor barrier and weatherproof coating designed for the protection of sprayed, board and block type insulation. ENCACEL V Vapor Barrier Coating has outstanding adhesive properties and excellent flexibility, in addition to its superior vapor barrier characteristics.
|
USES:
CP-45 is a finish for all cold insulation systems. It is also recommended for hot exterior sprayed polyurethane applications. In both cases, ENCACEL V Vapor Barrier Coating is used as the finish coat after flashing and sealing all metal protrusions throughout the surface of the insulation. ENCACEL V Vapor Barrier Coating can be used as a decorative finish over closed-cell flexible cellular plastics. Care must be taken that the adhesive bonded joint is not adversely affected by the solvent in the vapor barrier. It is not to be used in direct contact with polystyrene foam insulation.
COLOR:
CP-45 White, Spray/Brush
CP-45-1 Gray, Spray/Brush
SERVICE TEMPERATURE RANGE:
-50ºF to 220ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
Touch–3-4 hours
Through–24 hours
COVERAGE:
6 gal./100 sf
CLEAN-UP:
Xylene or Clorinated solvent
(Dried Encacel is extremely difficult to remove.)
WATER VAPOR PERMEANCE:
ASTM E 96, Method E, 0.025 perms
(0.016 metric perms) at 51 mils dry
ASTM E-96 Procedure A, 0.018 perms at 26 mils dry
ASTM F 1249, 0.05 perms at 30 mils dry. Tested at 100ºF and 90% RH.
|
|
|
CHILDERS CP-50A MV1 CHIL-SEAL
|
|
COMBINATION COATING AND ADHESIVE FOR FINISHING AND ADHERING CANVAS AND OTHER LAGGING CLOTHS OVER THERMAL INSULATION
DESCRIPTION:
Childers CHIL-SEAL CP-50A MV1 Coating is a white coating which is also an excellent adhesive. It brushes easily and yet forms a tough film even over surfaces such as glass cloth or canvas. Being a water based material, it is safe to use; it does not attack plastic foams or other adhesives. Brushes and tools are easily cleaned with water. CHILSEAL CP-50A MV1 Coating is fire resistive. It is also available in Marine Grade (CP-50A HV2 Coating), which meets MIL-A-3316 specification and USCG 164.012.
|
USES:
CHIL-SEAL CP-50A MV1 Coating is used for adhering fabrics such as glass cloth, canvas (up to 8 oz.) and brattice cloth to many insulated surfaces such as round and rectangular duct work and equipment. It is also used for adhering the laps of these fabrics as well as some woven glass cloths on pipe insulation. CHIL-SEAL CP-50A MV1 Coating is used as a coating over all of the above mentioned fabrics and also finds use as a coating over plastic foam materials such as polystyrene. CHIL-SEAL CP-50A MV1 Coating can be brushed on the joints of duct liner insulation to help prevent air erosion of the glass fiber.
COLOR:
White
SERVICE TEMPERATURE RANGE:
-20ºF to 180ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
To Touch–3 hours
Through–12 to 36 hours
COVERAGE:
1.0-1.25 U.S. Gal./100 sf per coat on canvas.
1.25-2.50 U.S. Gal./100 sf per coat on brattice cloth.
1.0 U.S. Gal./100 sf per coat on smooth dense surfaces.
CLEAN-UP:
Warm, soapy water (wet) Mineral Spirits (dry)
WATER VAPOR PERMEANCE:
ASTM F 1249, 0.07 perms at 27 mils dry. Tested at 100ºF and 90% RH.
SURFACE BURNING CHARACTERISTICS (ASTM E-84, U.L. TUNNEL TEST)
Flame Spread 10
Smoke Develop 0
|
|
|
CHILDERS CP-50A HV2 CHIL-SEAL
HIGH VISCOSITY COATING AND ADHESIVE FOR FINISHING AND ADHERING CANVAS AND OTHER LAGGING CLOTHS OVER THERMAL INSULATION
|
|
Meets Military Specification MIL-A-3316C, Class 1, Grade A
DESCRIPTION:
Childers CHIL-SEAL CP-50A HV2 Coating is a high viscosity white coating of heavy cream-like consistency which is also an excellent adhesive. It brushes easily and yet forms a tough film even over surfaces such as glass cloth or canvas. Being a water based material, it is safe to use; it does not attack plastic foams or other adhesives. Brushes and tools are easily cleaned with water.
|
USES:
CHIL-SEAL CP-50A HV2 coating is used for adhering fabrics such as glass cloth, canvas (up to 8 oz.) and brattice cloth to many insulated surfaces such as round and rectangular duct work and equipment. It is also used for adhering the laps of these fabrics as well as some woven glass cloths on pipe insulation. CHIL-SEAL CP-50A HV2 Coating is used as a coating over all of the above mentioned fabrics and also finds use as a coating over plastic foam materials such as polystyrene. CHIL-SEAL CP-50A HV2 Coating can be brushed on the joints of duct liner insulation to help prevent air erosion of the glass fiber.
COLORS:
White
SERVICE TEMPERATURE RANGE:
-20ºF to 180ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
Touch–2 Hours
Through–12 to 36 Hours
COVERAGE:
1.0-1.25 U.S. Gal./100 sf per coat on canvas.
1.25-2.50 U.S. Gal./100 sf per coat on brattice cloth.
1.0 U.S. Gal./100 sf per coat on smooth dense surfaces.
CLEAN-UP:
Warm, soapy water (wet) Mineral Spirits (dry)
WATER VAPOR PERMEANCE ASTM E-96
1.0 perms (Procedure B)
|
|
|
CHILDERS CP-56 CHIL-SPRAY WB
|
|
SPRAYABLE, WATER BASED PRESSURE SENSITIVE INSULATION ADHESIVE
DESCRIPTION:
Childers CHIL-SPRAY WB CP-56 is a fast tacking, adhesive specifically designed for application using conventional spray equipment. It aggressively bonds to any surface to which it is applied. The adhesive provides a tacky, permanently pressure sensitive film, which increases in strength with aging and resists creep.
|
USES:
CHIL-SPRAY CP-56 adhesive is used to bond lightweight insulation materials, including polystyrene, to duct work, and in equipment such as air conditioners, furnaces, or wherever insulation is bonded to metal. It is an excellent choice for bonding FSK and ASJ facings to board stock, blanket and piper covering insulation. CHIL-SPRAY CP-56 adhesive is also used to bond such porous and lightweight materials as cork, cardboard and paper. It may also be used in any application where a permanently tacky adhesive is required.
COLOR:
Cream
SERVICE TEMPERATURE RANGE:
-30ºF to 160ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
BONDING TIME:
5 to 60 minutes
COVERAGE:
For Insulation Attachment:
600-1000 sq. ft/U.S. Gallon
(adhesive applied to metal)
CLEAN-UP:
Warm, soapy water (wet), Mineral Spirits (dry)
|
|
|
CHILDERS CP-70 CHIL-JOINT
|
|
FLEXIBLE JOINT SEALANT, FLASHING COMPOUND AND VAPOR SEAL
DESCRIPTION:
Childers CHIL-JOINT CP-70 is a non-shrinking, permanently flexible, economical sealant for applications with all types of low temperature, dual temperature, and some high temperature insulation systems.
|
USES:
CHIL-JOINT CP-70 Sealant is used to vapor seal and act as an expansion joint in the joints of cellular glass and cellular plastic insulations. It will not attack even polystyrene insulations and remains flexible and functional through a wide temperature range. CHIL-JOINT CP-70 Sealant has good resistance to elevated temperatures, and it is recommended as an expansion joint material up to 300ºF. It is an excellent water seal, vapor seal and expansion joint material, and is suggested as a joint sealant for all metal jacketing systems.
COLOR:
Gray
SERVICE TEMPERATURE RANGE:
-100ºF to 300ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
DRYING TIME:
Non-Drying: Skins over in 24 hours
FLASH POINT:
142ºF
COVERAGE:
For Joint: 1” x 1/16” = 1 U.S. gal. for 308 lin. ft.
125 lin. ft. per 10.5 oz. tube for 1/8” bead
COMBUSTIBILITY:
Combustible. Flame spread and fuel contribution negligible when used as sealant in 1/8 in. wide joints of incombustible insulation.
CLEAN-UP:
Mineral spirits
WATER VAPOR PERMEANCE:
ASTM F-1249, 0.06 perm (0.04 metric perm) tested
in 1/8” film at 100ºF and 90%RH
|
|
|
CHILDERS CP-79 CHIL-LASTIC
|
|
HIGH TEMPERATURE ASPHALT SEALANT AND COATING
DESCRIPTION:
Childers CHIL-LASTIC CP-79 is a multi-purpose high temperature sealant and coating. It is applied by trowel over all types of thermal insulations. Do not use in conjunction with polystyrene. Being an asphalt based coating, CHIL-LASTIC CP-79 forms a tough, durable, heavy film when applied. It can be used at elevated temperatures. CHIL-LASTIC CP-79 sealant/coating should be allowed to cure at ambient temperature with thorough ventilation before hot lines, vessels, or tanks are put into operation. Failure to do so may increase the possibility of residual solvent boiling out of the film.
|
USES:
CHIL-LASTIC CP-79 sealant/coating is used as flashing material in the sealing of boiler settings to prevent air infiltration. It is also used in refractory applications.
COLOR:
Black
SERVICE TEMPERATURE RANGE:
-75ºF to 350ºF
APPLICATION TEMPERATURE RANGE:
50ºF to 100ºF
DRYING TIME:
Touch–4-8 hours
Through–14 days
COVERAGE:
CP-79-T 8 gallons per 100 sf
0.128” wet film thickness.
CP-79-S 10 gallons per 100 sf
0.160” wet film thickness
FLASH POINT:
Over 100ºF
VAPOR PERMEABILITY:
0.01 grains/hour/sq. ft./in. (Perm)
CLEAN-UP:
Mineral Spirits
|
|
|
CHILDERS CP-82 CHIL-STIX FRN ADHESIVE
|
|
FIRE RESISTIVE, NON-FLAMMABLE NEOPRENE BASE CONTACT ADHESIVE FOR VAPOR BARRIER LAPS AND INSULATIONS
DESCRIPTION:
Childers Chil-Stix FRN CP-82 is a neoprene based contact adhesive with exceptional bond strength. It is non-flammable in the wet state and meets the performance requirements of Military Specification MIL-A-3316C, Class 2, Grade A.
|
USES:
Childers CHIL-STIX FRN CP-82 adhesive is ideal for adhering many types of insulations such as fibrous glass, laminated scrims, foils, many plastic films, and various foams, both flexible and rigid. The solvents in this adhesive will attack polystyrene foams and may attack certain other plastic foams, plastic films, and plastic laminates. CHIL-STIX FRN CP-82 adhesive effectively adheres the laps of most types of vapor barrier jackets. Because of its superior contact properties it finds many uses both inside and outside of the insulation industry.
COLOR:
Light tan
SERVICE TEMPERATURE RANGE:
-30ºF to 200ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
BONDING TIME:
0 to 5 minutes - 1 surface
20 minutes to 1 hour - contact
COVERAGE:
150 to 250 sf / gallon
For Sealing 2” wide Laps:
600 to 750 linear feet / gallon
CLEAN-UP:
Chlorinated Solvents or Xylene
|
|
|
CHILDERS CP-85 CHIL-STIX ADHESIVE
|
|
QUICK SETTING RUBBER ADHESIVE FOR FLEXIBLE BLANKET INSULATIONS AND VAPOR BARRIER FACINGS
DESCRIPTION:
Childers CHIL-STIX CP-85 adhesive is a fast drying rubber based adhesive with quick initial grab. It remains permanently flexible.
|
USES:
Childers CP-85 adhesive adheres low density fibrous glass insulations, some plastic foams, and other light density materials to sheet metal surfaces such as galvanized steel and aluminum. It may be used to bond many facings and fabrics to each other and to a variety of substrates. CHIL-STIX CP-85 adhesive is used for adhering to laps of vapor barrier jackets and facings.
COLOR:
Clear Amber
SERVICE TEMPERATURE RANGE:
-20ºF to 200ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
BONDING TIME:
For Insulation Attachment: 0 to 10 minutes
For Lap Sealing: 2 to 10 minutes
COVERAGE:
For Insulation Attachment:
200 to 250 sf / gallon
(Adhesive applied to metal)
For Sealing 2” wide Laps:
500 to 600 linear feet / gallon
CLEAN-UP:
Chlorinated Solvents or Mineral spirits
|
|
|
CHILDERS CP-96 CHIL-RENE ADHESIVE
|
|
HIGH STRENGTH POLYSTYRENE AND POLYURETANE ADHESIVE
DESCRIPTION:
Childers CHIL-RENETM CP-96 is high strength solvent based fast grab synthetic rubber and resin adhesive specifically designed to adhere extruded and expanded rigid polystyrene and all urethane insulations to themselves and to other porous and non-porous substrates. It exhibits good initial tack and sets up quickly.
|
USES:
Childers CHIL-RENE CP-96 adhesive is used to bond polystyrene and polyurethane to itself and other structural surfaces including aluminum, stainless steel, galvanized steel, concrete block, ceramic tile, masonry, drywall, wood, and gypsum board. It may also be used to adhere semirigid fiberglass insulation to a substrate. When bonding insulation to surfaces other than those listed above, a small test patch is recommended to assure compatibility. CHIL-RENE CP-96 adhesive is not recommended when impervious surfaces need to be bonded together.
COLOR:
Light Tan
SERVICE TEMPERATURE RANGE:
-20ºF to 180ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
BONDING TIME:
1 to 10 minutes.
COVERAGE:
60 sf/gal - Trowel
CLEAN-UP:
Mineral Spirits or Chlorinated Solvents
FLAMMABILITY:
FLAMMABLE in the wet state
|
|
|
CHILDERS CP-97 FIBROUS ADHESIVE
|
|
NON-FLAMMABLE QUICK SETTING ADHESIVE FOR CALCIUM SILICATE AND OTHER INSULATIONS
DESCRIPTION:
Childers FIBROUS ADHESIVE CP-97 is a sodium silicate base adhesive of exceptional strength. It is non-flammable in the wet state and is totally incombustible in the dry state.
|
USES:
Childers CP-97 is used to bond dense thermal insulations such as calcium silicate and expanded perlite to itself and to non-porous surfaces. Primed or painted metal surfaces should be tested for compatibility with FIBROUS ADHESIVE CP-97 prior to use. It will also effectively adhere other ‘hard to hold’ materials. Because of its sodium silicate base, this product is not recommended for use with glass fiber or other alkali sensitive insulations.
COLOR:
Gray
SERVICE TEMPERATURE RANGE:
40ºF to 850ºF
APPLICATION TEMPERATURE RANGE:
40ºF to 100ºF
BONDING TIME:
0 TO 5 minutes
DRYING TIME:
1 hour
COVERAGE:
2.5-3.0 gallons / 100 sf
DRY COMBUSTIBILITY:
Incombustible
CLEAN-UP:
Warm soapy water.
|
|
|
|